THỬ NGHIỆM ANOT MAGNETITE TRONG HỆ THỐNG BẢO VỆ ĐIỆN HÓA CHỐNG ĂN MÒN VỎ THÉP TÀU BIỂN
Nội dung chính của bài viết
Tóm tắt
TESTING OF MAGNETITEANODE USED IN THE ELECTROCHEMICAL SYSTEM TO PREVENT CORROSION OF STEEL HULL IN SEAWATER
The paper presents the testing results of magnetite anode used in the impressed current cathodic protection system to prevent corrosion of steel hull in the seawater at Nha Trang bay. Testing results for steel hull with an submerged area of ~ 300 m2 in seawater showed that anodic current reached 0.7 ÷ 1.5 A, the largest anodic current density reached ~ 764 A/m2, the voltage shift of hull is from -156 mV to -259 mV. The voltage of the hull compared to Ag/AgCl reference electrode meets cathodic protection standards in the seawater.
Từ khóa
Anot magnetite, bảo vệ catot dòng điện ngoài, chống ăn mòn, magnetite anode, the impressed current cathodic protection, corrosion
Chi tiết bài viết
Tài liệu tham khảo
2. Phan Lương Cầm, Hoàng Thị Bích Thủy, Chống ăn mòn cho công trình thép và bê tông cốt thép bằng phương pháp bảo bệ catot, Hội thảo Môi trường nhiệt đới Việt Nam với vấn đề ăn mòn và bảo vệ kim loại, TP. HCM, 1997, tr.7-16.
3. James B. Bushman, Corrosion and cathodic protection theory, Bushman & Associates Inc., Medina, Ohio, USA, 2010.
4. Trịnh Xuân Sén, Ăn mòn và bảo vệ kim loại, NXB ĐHQG Hà Nội, 2006.
5. TCVN 6170-8:1999, Công trình biển cố định, Kết cấu, Phần 8, Hệ thống chống ăn mòn, NXB Xây dựng, Hà Nội, 2001.
6. Nguyễn Hồng Dư, Lưu Phương Minh, Nguyễn Trọng Hiệp, Khảo sát một số tính chất điện hóa của anot magnetit được chế tạo theo phương pháp luyện kim bột, Tạp chí KH&CN Nhiệt đới, Số 1, 12/2012.
7. W. Von Baeckmann, W. Schwenk and W. Prinz, Handbook of cathodic corrosion protection, Theory and practice of electrochemical protection processes, third edition, 1997, p.209-214.
8. Ngô Quốc Quyền & cs., Nghiên cứu độ bền ăn mòn của hợp kim bằng phương pháp phổ tổng trở điện hóa, Tạp chí Hóa học, 2003, 41, tr.6-12.